The hardness of bainite can be between that of pearlite and untempered martensite in the same steel hardness. The fact that it can be produced during both isothermal or continuous cooling is a big advantage, because this facilitates the production of large components without excessive additions of alloying elements.
Pearlite is a two-phased, lamellar (or layered) structure composed of alternating layers of ferrite (87.5 wt%) and cementite (12.5 wt%) that occurs in some steels and cast irons. During slow cooling of an iron-carbon alloy, pearlite forms by a eutectoid reaction as austenite cools below 723 °C (1,333 °F) (the eutectoid temperature).
Thereafter, the decrease in diffusion rate due to low temperature offsets the effect of increased driving force due to greater difference in free energy. As a result of the transformation, the microconstituents, pearlite and bainite, form; pearlite forms at higher temperatures and bainite at lower.
Austempering is a technique used to form pure bainite, a transitional microstructure found between pearlite and martensite. In normalizing, both upper and lower bainite are usually found mixed with pearlite. To avoid the formation of pearlite or martensite, the steel is quenched in a bath of molten metals or salts.
This microstructure is referred to as "sphereoidite". If cooled a little faster, then coarse pearlite will form. Even faster, and fine pearlite will form. If cooled even faster, bainite will form, with more complete bainite transformation occurring depending on the time held above martensite start Ms. Similarly, these microstructures will also ...
A tempered outer ring of martensite, 2. A semi-tempered middle ring of martensite and bainite, and 3. a mild circular core of bainite, ferrite and pearlite. This is the desired micro structure for quality construction rebar. In contrast, lower grades of rebar are twisted when cold, work hardening them to increase their strength.
The search engine that helps you find exactly what you're looking for. Find the most relevant information, video, images, and answers from all across the Web.
In steel it produces a bainite microstructure whereas in cast irons it produces a structure of acicular ferrite and high carbon, stabilized austenite known as ausferrite. It is primarily used to improve mechanical properties or reduce / eliminate distortion. Austempering is defined by both the process and the resultant microstructure.