Pearlite is a two-phased, lamellar (or layered) structure composed of alternating layers of ferrite (87.5 wt%) and cementite (12.5 wt%) that occurs in some steels and cast irons. During slow cooling of an iron-carbon alloy, pearlite forms by a eutectoid reaction as austenite cools below 723 °C (1,333 °F) (the eutectoid temperature).
This increases the brittleness of the steel in a way that can only be relieved by recrystallizing. Widmanstätten structures made from ferrite sometimes occur in carbon steel, if the carbon content is below but near the eutectoid composition (~ 0.8% carbon). This occurs as long needles of ferrite within the pearlite. [16]
Under a light microscope, the microstructure of bainite appears darker than untempered martensite because the bainite has more substructure. [9] The hardness of bainite can be between that of pearlite and untempered martensite in the same steel hardness. The fact that it can be produced during both isothermal or continuous cooling is a big ...
Below 912 °C (1,674 °F), iron has a body-centered cubic (bcc) crystal structure and is known as α-iron or ferrite.It is thermodynamically stable and a fairly soft metal. α-Fe can be subjected to pressures up to ca. 15 GPa before transforming into a high-pressure form termed ε-Fe discussed below.
The study of microscopic anatomy (or histology) can be aided by practical experience examining histological preparations (or slides) under a microscope; and in addition, medical and dental students generally also learn anatomy with practical experience of dissection and inspection of cadavers (dead human bodies).
A very rapid quench is essential to create martensite. For a eutectoid carbon steel of thin section, if the quench starting at 750 °C and ending at 450 °C takes place in 0.7 seconds (a rate of 430 °C/s) no pearlite will form, and the steel will be martensitic with small amounts of retained austenite. [2]
They are often observed in cases where a phase transition front moves quickly, leaving behind two solid products, as in rapid cooling of eutectic (such as solder) or eutectoid (such as pearlite) systems. Such conditions force phases of different composition to form but allow little time for diffusion to produce those phases' equilibrium ...
[2] [3] Acicular ferrite is a fine Widmanstätten constituent, which is nucleated by an optimum intragranular dispersion of oxide/sulfide/silicate particles. The interlocking nature of acicular ferrite, together with its fine grain size (0.5 to 5 μm with aspect ratio from 3:1 to 10:1), provides maximum resistance to crack propagation by cleavage.