The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Probability density of stress S (red, top) and resistance R (blue, top), and of equality (m = R - S = 0, black, bottom). Distribution of stress S and strength R: all the (R, S) situations have a probability density (grey level surface). The area where the margin m = R - S is positive is the set of situation where the system is reliable (R > S).
The strength of materials is determined using various methods of calculating the stresses and strains in structural members, such as beams, columns, and shafts. The methods employed to predict the response of a structure under loading and its susceptibility to various failure modes takes into account the properties of the materials such as its yield strength, ultimate strength, Young's modulus ...
It is also known as the strength-to-weight ratio or strength/weight ratio or strength-to-mass ratio. In fiber or textile applications, tenacity is the usual measure of specific strength. The SI unit for specific strength is Pa ⋅ m 3 / kg , or N ⋅m/kg, which is dimensionally equivalent to m 2 /s 2 , though the latter form is rarely used.
Huber's equation, first derived by a Polish engineer Tytus Maksymilian Huber, is a basic formula in elastic material tension calculations, an equivalent of the equation of state, but applying to solids. In most simple expression and commonly in use it looks like this: [1]
Specific strength: Strength per unit density (Nm/kg) Specific weight: Weight per unit volume (N/m^3) Surface roughness: The deviations in the direction of the normal vector of a real surface from its ideal form; Tensile strength: Maximum tensile stress of a material can withstand before failure (MPa)
Fig. 1: Critical stress vs slenderness ratio for steel, for E = 200 GPa, yield strength = 240 MPa. Euler's critical load or Euler's buckling load is the compressive load at which a slender column will suddenly bend or buckle. It is given by the formula: [1] = where
In materials science, a general rule of mixtures is a weighted mean used to predict various properties of a composite material. [1] [2] [3] It provides a theoretical upper- and lower-bound on properties such as the elastic modulus, ultimate tensile strength, thermal conductivity, and electrical conductivity. [3]