When melting points of the monomers are sufficiently low, a polyester can be formed via direct esterification while removing the reaction water via vacuum. Direct bulk polyesterification at high temperatures (150 – 290 °C) is well-suited and used on the industrial scale for the production of aliphatic, unsaturated, and aromatic–aliphatic ...
Polycaprolactone (PCL) is a synthetic, semi-crystalline, biodegradable polyester with a melting point of about 60 °C and a glass transition temperature of about −60 °C. [2] [3] The most common use of polycaprolactone is in the production of speciality polyurethanes.
This interferes with crystallization and lowers the polymer's melting temperature. In general, such PET is known as PETG or PET-G (polyethylene terephthalate glycol-modified). It is a clear amorphous thermoplastic that can be injection-molded, sheet-extruded or extruded as filament for 3D printing .
Polybenzimidazole (PBI, short for Poly-[2,2’-(m-phenylen)-5,5’-bisbenzimidazole]) fiber is a synthetic fiber with a very high melting point. It has exceptional thermal and chemical stability and does not readily ignite.
Polyester resins are synthetic resins formed by the reaction of dibasic organic acids and polyhydric alcohols. Maleic anhydride is a commonly used raw material with diacid functionality in unsaturated polyester resins. [1] Unsaturated polyester resins are used in sheet moulding compound, bulk moulding compound and the toner of laser printers.
Polyester is also a popular option since it’s non-flammable with a very high melting point, says Christian. For the pad’s fill, Wu also suggests organic materials, such as beans, rice, corn ...
Polyglycolide has a glass transition temperature between 35 and 40 °C and its melting point is reported to be in the range of 225 to 230 °C. PGA also exhibits an elevated degree of crystallinity, around 45–55%, thus resulting in insolubility in water. [2]
Polycyclohexylenedimethylene terephthalate (PCT) is a thermoplastic polyester formed from the polycondensation of terephthalic acid and cyclohexanedimethanol. [1] Its chemical structure is similar to that of polyethylene terephthalate (PET), with which it shares properties like dimensional stability and chemical resistance.