Polymer degradation is the reduction in the physical properties of a polymer, such as strength, caused by changes in its chemical composition.Polymers and particularly plastics are subject to degradation at all stages of their product life cycle, including during their initial processing, use, disposal into the environment and recycling. [1]
Accelerated photo-ageing of polymers in SEPAP units is the controlled polymer degradation and polymer coating degradation under lab or natural conditions. The prediction of the ageing of plastic materials is a subject that concerns both users and manufacturers.
Melting points and glass transition temperatures for most polymers are available from standard compilations, and the method can show polymer degradation by the lowering of the expected melting temperature. T m depends on the molecular weight of the polymer and thermal history. [citation needed]
In polymers, such as plastics, thermal degradation refers to a type of polymer degradation where damaging chemical changes take place at elevated temperatures, without the simultaneous involvement of other compounds such as oxygen. [1] [2] Simply put, even in the absence of air, polymers will begin to degrade if heated high enough. It is ...
Thus, degradation is accelerated and the test is less time-consuming. Through weather testing, the impact of photooxidative processes on the mechanical properties and lifetimes of polymer samples can be determined. For example, the tensile behavior can be elucidated through measuring the stress–strain curve for a specimen. This stress ...
Field-flow fractionation (FFF) can be considered as an alternative to GPC, especially when particles or high molar mass polymers cause clogging of the column, shear degradation is an issue or agglomeration takes place but cannot be made visible. FFF is separation in an open flow channel without having a static phase involved so no interactions ...
To determine whether a polymer will undergo surface or bulk erosion, the degradation rate of the polymer in water (how fast the polymer reacts to water) and the rate of diffusion of water penetrating through the material must be considered. If the degradation process is faster than the diffusion process, surface erosion will occur since the ...
The characterization of mechanical properties in polymers typically refers to a measure of the strength, elasticity, viscoelasticity, and anisotropy of a polymeric material. The mechanical properties of a polymer are strongly dependent upon the Van der Waals interactions of the polymer chains, and the ability of the chains to elongate and align ...