Carbonyl iron has lower losses than hydrogen-reduced iron, but also lower permeability. A popular application of carbonyl iron-based magnetic cores is in high-frequency and broadband inductors and transformers, especially higher power ones. Carbonyl iron cores are often called "RF cores".
Mu-metal is a soft magnetic alloy with exceptionally high magnetic permeability. The high permeability of mu-metal provides a low reluctance path for magnetic flux , leading to its use in magnetic shields against static or slowly varying magnetic fields.
For example, 4% electrical steel has an initial relative permeability (at or near 0 T) of 2,000 and a maximum of 38,000 at T = 1 [5] [6] and different range of values at different percent of Si and manufacturing process, and, indeed, the relative permeability of any material at a sufficiently high field strength trends toward 1 (at magnetic ...
Ferromagnetism is a property of certain materials (such as iron) that results in a significant, observable magnetic permeability, and in many cases, a significant magnetic coercivity, allowing the material to form a permanent magnet. Ferromagnetic materials are noticeably attracted to a magnet, which is a consequence of their substantial ...
Different materials have different saturation levels. For example, high permeability iron alloys used in transformers reach magnetic saturation at 1.6–2.2 teslas (T), [4] whereas ferrites saturate at 0.2–0.5 T. [5] Some amorphous alloys saturate at 1.2–1.3 T. [6] Mu-metal saturates at around 0.8 T. [7] [8]
Strip of permalloy. Permalloy is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content.Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, [1] it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields.
The most common soft ferrites are: Manganese-zinc ferrite (MnZn, with the formula Mn a Zn (1−a) Fe 2 O 4). MnZn have higher permeability and saturation levels than NiZn. Nickel-zinc ferrite (NiZn, with the formula Ni a Zn (1−a) Fe 2 O 4). NiZn ferrites exhibit higher resistivity than MnZn, and are therefore more suitable for frequencies ...
3, is in between soft and hard magnetic material and is usually classified as a semi-hard material. [23] It is mainly used for its magnetostrictive applications like sensors and actuators [24] thanks to its high saturation magnetostriction (~200 ppm). Co Fe 2 O 4 has also the benefits to be rare-earth free, which makes it a good substitute for ...