Depending on the temperature and composition of the steel, it can be hardened or softened. To make steel harder, it must be heated to very high temperatures. The final result of exactly how hard the steel becomes depends on the amount of carbon present in the metal. Only steel that is high in carbon can be hardened and tempered.
RHA is homogeneous because its structure and composition are uniform throughout its thickness. The opposite of homogeneous steel plate is cemented or face-hardened steel plate, where the face of the steel is composed differently from the substrate. The face of the steel, which starts as an RHA plate, is hardened by a heat-treatment process.
The quenched-steel is first sanded or polished, to remove any residual oxidation, revealing the bare metal underneath. The steel is then heated in a localized area, such as the hammering-end of a chisel or the handle-end of an axe. The smith then carefully gauges the temperature by watching the tempering colors of the steel. As the steel is ...
Martensitic transformation, more commonly known as quenching and tempering, is a hardening mechanism specific for steel. The steel must be heated to a temperature where the iron phase changes from ferrite into austenite, i.e. changes crystal structure from BCC (body-centered cubic) to FCC (face-centered cubic). In austenitic form, steel can ...
In diffusion hardening, diffusion occurs between a steel with a low carbon content and a carbon-rich environment to increase the carbon content of the steel and ultimately harden the workpiece. [ 1 ] [ 2 ] Diffusion only happens through a small thickness of a piece of steel (about 2.5 μm to 1.5 mm), so only the surface is hardened while the ...
When a hot steel work-piece is quenched, the area in contact with the water immediately cools and its temperature equilibrates with the quenching medium.The inner depths of the material however, do not cool so rapidly, and in work-pieces that are large, the cooling rate may be slow enough to allow the austenite to transform fully into a structure other than martensite or bainite.
Steel can be softened to a very malleable state through annealing, or it can be hardened to a state as hard and brittle as glass by quenching. However, in its hardened state, steel is usually far too brittle, lacking the fracture toughness to be useful for most applications. Tempering is a method used to decrease the hardness, thereby ...
The front plate was intended to break up an incoming shell, while the rear plate would catch any splinters and hold the armor together if the brittle front plate shattered. Compound armor was made by pouring molten steel between a red-hot wrought iron backing plate and a hardened steel front plate to weld them together. This process produced a ...