FEP; CAS Registry Number: 25067-11-2 Density [1] 2150 kg/m 3: Flexural modulus(E) 586 M Pa: Tensile strength(t) 23 M Pa: Elongation @ break 325% Folding endurance Varies Notch test Melting point: 260 °C Maximum operating temperature 204 °C Water absorption (ASTM) <0.01 % after 24 hours Dielectric constant (Dk) at 1M Hz: 2.1 Dissipation factor
When melting points of the monomers are sufficiently low, a polyester can be formed via direct esterification while removing the reaction water via vacuum. Direct bulk polyesterification at high temperatures (150 – 290 °C) is well-suited and used on the industrial scale for the production of aliphatic, unsaturated, and aromatic–aliphatic ...
Polycyclohexylenedimethylene terephthalate (PCT) is a thermoplastic polyester formed from the polycondensation of terephthalic acid and cyclohexanedimethanol. [1] Its chemical structure is similar to that of polyethylene terephthalate (PET), with which it shares properties like dimensional stability and chemical resistance.
That point determines the processing temperatures needed to shape the material, as well as the ultimate service use temperatures of the product. Such materials include Hytrel, a polyester-polyether copolymer and Pebax , a nylon or polyamide-polyether copolymer.
The onset of thermal degradation dictates the maximum temperature at which a polymer can be used. It is an important limitation in how the polymer is manufactured and processed. For instance, polymers become less viscous at higher temperatures which makes injection moulding easier and faster, but thermal degradation places a ceiling temperature ...
General chemical structure of a polyketone. Polyketones are a family of high-performance thermoplastic polymers. The polar ketone groups in the polymer backbone of these materials gives rise to a strong attraction between polymer chains, which increases the material's melting point (255 °C for copolymer (carbon monoxide ethylene), 220 °C for terpolymer (carbon monoxide, ethylene, propylene).
Tests showed the substance was resistant to corrosion from most acids, bases and solvents and had better high temperature stability than any other plastic. By early 1941, a crash program was making substantial quantities of PTFE for the Manhattan Project. [1] [2] [3] [4]
Polybenzimidazole (PBI, short for Poly-[2,2’-(m-phenylen)-5,5’-bisbenzimidazole]) fiber is a synthetic fiber with a very high melting point. It has exceptional thermal and chemical stability and does not readily ignite.