There are three basic techniques that may be used to attach granules to a metal surface: hard soldering, fusing and colloidal soldering. The metals used in granulation are usually gold and/or silver alloys of high purity – alloys below 18 kt. gold and sterling silver being unsuitable. With each technique, the process begins with the making of ...
Although the method used is called soldering, it is actually a form of brazing, using "solders" of the metal being worked, i.e. gold solders for gold pieces, silver solder for silver pieces, etc. All of this is the work of bench jewelers, who at this level are sometimes known as production workers in some arenas.
Extra-easy solder contains 56% silver and has a melting point of 618 °C (1,145 °F). Extra-hard solder has 80% silver and melts at 740 °C (1,370 °F). If multiple joints are needed, then the jeweler will start with hard or extra-hard solder and switch to lower-temperature solders for later joints. Silver solder is somewhat absorbed by the ...
This Roman jewelry is dated to approximately 2,000 years ago. In the manufacture of this early jewelry the techniques for soldering did not exist. Later, as the technique for soldering developed, the wire wrapping approach continued because it was an economical and quick way to make jewelry components out of wire.
Yemenite silver-work is noted for its intricate use of filigree and fine granulation. [2] [6] Jewellery containing a high silver content was called ṭohōr by local Jews, or muḫlaṣ in Arabic, and referred to jewellery whose silver content ranged from 85 to 92 percent, while the rest was copper.
Sterling silver is an alloy composed by weight of 92.5% silver and 7.5% other metals, usually copper. The sterling silver standard has a minimum millesimal fineness of 925. Tiffany & Co. pitcher ( c. 1871 ) having paneled sides and repoussé design with shells, scrolls and flowers; top edge is repousse arrowhead leaf design
In jewelry making, pickling is used to remove the copper oxide layer that results from heating copper and sterling silver during soldering and annealing. A diluted sulfuric acid pickling bath is traditionally used, [ 6 ] but may be replaced with citric acid .
Silversmiths saw or cut specific shapes from sterling and fine silver sheet metal and bar stock; they then use hammers to form the metal over anvils and stakes. Silver is hammered cold (at room temperature). As the metal is hammered, bent, and worked, it 'work-hardens'. Annealing is the heat-treatment used to make the metal soft again. If metal ...