Tempered or toughened glass is a type of safety glass processed by controlled thermal or chemical treatments to increase its strength compared with normal glass. Tempering puts the outer surfaces into compression and the interior into tension .
Toughened glass is processed by controlled thermal or chemical treatments to increase its strength compared with normal glass. [6] Tempering, by design, creates balanced internal stresses which causes the glass sheet, when broken, to crumble into small granular chunks of similar size and shape instead of splintering into random, jagged shards.
These are the result of the relatively "naked" designs produced by manufacturers such as Apple, where the metal and glass components of the device are exposed and vulnerable to damage. They are distinct from holsters, in allowing use of the device while in the case, but in many instances include a belt clip or other device giving it the ...
Also unlike toughened glass, chemically strengthened glass may be cut after strengthening, but loses its added strength within approximately 20 mm of the cut. Similarly, when the surface of chemically strengthened glass is deeply scratched, this area loses its additional strength. Another negative of chemically strengthened glass is the added cost.
A Nokia N8 with a Gorilla Glass screen. Gorilla Glass, developed and manufactured by Corning, is a brand of chemically strengthened glass now in its ninth generation. Designed to be thin, light, and damage-resistant, its surface strength and crack-resistance are achieved through immersion in a hot potassium-salt ion-exchange bath.
The top and side of an iPhone 5S, externally identical to the SE (2016).From left to right, sides: wake/sleep button, silence switch, volume up, and volume down. The touchscreen on the iPhone has increased in size several times over the years, from 3.5 inches on the original iPhone to iPhone 4S, to the current 6.1 and 6.7 inches on the iPhone 14 and 14 Pro series. [1]
Float glass is a sheet of glass made by floating molten glass on a bed of molten metal of a low melting point, typically tin, [1] although lead was used for the process in the past. [2] This method gives the sheet uniform thickness and a very flat surface. [ 3 ]
Glass fibers have a much higher tensile strength than regular glass (200-500 times stronger than regular glass). [7] This is due to the reduction of flaws in glass fibers [8] and the small cross sectional area of glass fibers, constraining maximum defect size. [2]