When it reacts with concrete, it causes the slab to expand, lifting, distorting and cracking as well as exerting a pressure onto the surrounding walls which can cause movements significantly weakening the structure. Some infill materials frequently encountered in building fondations and causing sulfate attack are the following: [2] Red Ash
ASTM C1293: "Test Method for Concrete Aggregates by Determination of Length Change of Concrete Due to Alkali-Silica Reaction". It is a long-term confirmation test (1 or 2 years) at 38 °C in a water-saturated moist atmosphere (inside a thermostated oven) with concrete prisms containing the aggregates to be characterised mixed with a high-alkali ...
If concrete is exposed to very high temperatures very rapidly, explosive spalling of the concrete can result. In a very hot, very quick fire the water inside the concrete will boil before it evaporates. The steam inside the concrete exerts expansive pressure and can initiate and forcibly expel a spall. [23]
The second barrier is due to the precipitation, when the surficial pH gets below 10, of a layer of alumina gel (AH3 in cement chemistry notation). AH3 is a stable compound down to a pH of 4 and it will form an acid-resistant barrier as long as the surface pH is not lowered below 3–4 by the bacterial activity.
Samples of "ground granulated blast furnace slag" (left) and "granulated blast furnace slag" (right) Ground granulated blast-furnace slag (GGBS or GGBFS) is obtained by quenching molten iron slag (a by-product of iron and steel-making) from a blast furnace in water or steam, to produce a glassy, granular product that is then dried and ground into a fine powder.
Conversely, concrete is one of the most powerful tools for proper flood control, by means of damming, diversion, and deflection of flood waters, mud flows, and the like. Light-colored concrete can reduce the urban heat island effect, due to its higher albedo. [3] However, original vegetation results in even greater benefit.
The chemical processes of Portland cement hydration lead to another type of shrinkage, called the autogeneous shrinkage, which is observed in sealed specimens, i.e., at no moisture loss. It is caused partly by chemical volume changes, but mainly by self-desiccation due to loss of water consumed by the hydration reaction.
Aerial photograph from Popular Mechanics magazine, 1921. The Oppau explosion occurred on September 21, 1921, when approximately 4,500 tonnes of a mixture of ammonium sulfate and ammonium nitrate fertilizer stored in a tower silo exploded at a BASF plant in Oppau, now part of Ludwigshafen, Germany, killing 500–600 people and injuring about 2,000 more.