Search results
Results from the WOW.Com Content Network
Tensile test of an Al-Mg-Si alloy. The local necking and the cup and cone fracture surfaces are typical for ductile metals. This tensile test of a nodular cast iron demonstrates low ductility. Ductility refers to the ability of a material to sustain significant plastic deformation before fracture. Plastic deformation is the permanent distortion ...
Ductility: Ability of a material to deform under tensile load (% elongation). It is the property of a material by which it can be drawn into wires under the action of tensile force. A ductile material must have a high degree of plasticity and strength so that large deformations can take place without failure or rupture of the material.
A general parameter that indicates the formability and ductility of a material is the fracture strain which is determined by a uniaxial tensile test (see also fracture toughness). The strain identified by this test is defined by elongation with respect to a reference length.
Because the local strains in the neck are large, necking is often closely associated with yielding, a form of plastic deformation associated with ductile materials, often metals or polymers. [1] Once necking has begun, the neck becomes the exclusive location of yielding in the material, as the reduced area gives the neck the largest local stress .
Work hardening occurs most notably for ductile materials such as metals. Ductility is the ability of a material to undergo plastic deformations before fracture (for example, bending a steel rod until it finally breaks). The tensile test is widely used to study deformation mechanisms. This is because under compression, most materials will ...
Stress–strain curve for brittle materials compared to ductile materials. Some common characteristics among the stress–strain curves can be distinguished with various groups of materials and, on this basis, to divide materials into two broad categories; namely, the ductile materials and the brittle materials. [1]: 51
Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
ductility (by elongation to fracture or the reduction of the area) ultimate tensile strength (from the maximum load) area under the elongation - load curve (which represents the fracture energy) percent of ductile/brittle fracture on the fracture surface; threshold stress for cracking; The results of the SSRT tests are evaluated using the ratio: