The SAE steel grades system is a standard alloy numbering system (SAE J1086 – Numbering Metals and Alloys) for steel grades maintained by SAE International.. In the 1930s and 1940s, the American Iron and Steel Institute (AISI) and SAE were both involved in efforts to standardize such a numbering system for steels.
In addition to the descriptive steel grade naming system indicated above, within EN 10027-2 is defined a system for creating unique steel grade numbers. While less descriptive and intuitive than the grand names they are easier to tabulate and use in data processing applications.
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...
ISO 18265: "Metallic materials — Conversion of hardness values" (2013) ASTM E140-12B(2019)e1: "Standard Hardness Conversion Tables for Metals Relationship Among Brinell Hardness, Vickers Hardness, Rockwell Hardness, Superficial Hardness, Knoop Hardness, Scleroscope Hardness, and Leeb Hardness" (2019)
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
Stainless steel, also known as inox, corrosion-resistant steel (CRES), or rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5% or more chromium content, which forms a passive film that can protect the material ...
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]
MIL-DTL-46100E specifies a steel of identical hardness. [3] MIL-DTL-32332 specifies ultra-hard steel, with Brinell hardness in excess of 570. [3] A Chinese publication lists 30MnCrNiMo "685" steel as the material used in Chinese rolled armor plates, with a Brinell Hardness of HBW 444-514 (thin) / 429-495 (thick).