Concrete cone is one of the failure modes of anchors in concrete, loaded by a tensile force. The failure is governed by crack growth in concrete, which forms a typical cone shape having the anchor's axis as revolution axis .
The test is carried out using a metal mould in the shape of a conical frustum known as a slump cone or Abrams cone, that is open at both ends and has attached handles.The tool typically has an internal diameter of 100 millimetres (3.9 in) at the top and of 200 millimetres (7.9 in) at the bottom with a height of 305 millimetres (12.0 in).The cone is placed on a hard non-absorbent surface.
The cone is placed in the center of the flow table and filled with fresh concrete in two equal layers. Each layer is tamped 10 times with a tamping rod. Wait 30 seconds before lifting the cone. The cone is lifted, allowing the concrete to flow. The flow table is then lifted up 40mm and then dropped 15 times, causing the concrete to flow.
Concrete cone: after reaching the load-bearing capacity a cone shape is formed. The failure is governed by crack growth in concrete. [15] This kind of failure is typical in pull-out test. [16] [17] Splitting failure: failure is characterized by a splitting crack which divides the base material into two parts.
Concrete fracture analysis is part of fracture mechanics that studies crack propagation and related failure modes in concrete. [17] As it is widely used in construction, fracture analysis and modes of reinforcement are an important part of the study of concrete, and different concretes are characterized in part by their fracture properties. [ 18 ]
A pronounced energetic size effect occurs in shear, torsional and punching failures of reinforced concrete, in pullout of anchors from concrete, in compression failure of slender reinforced concrete columns and prestressed concrete beams, in compression and tensile failures of fiber-polymer composites and sandwich structures, and in the ...
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
In materials science, material failure is the loss of load carrying capacity of a material unit. This definition introduces to the fact that material failure can be examined in different scales, from microscopic, to macroscopic. In structural problems, where the structural response may be beyond the initiation of nonlinear material behaviour ...