It cannot be work hardened, but is commonly heat treated to produce tempers with a higher strength but lower ductility. [1] Alternate names and designations include AlSi1MgMn, 3.2315, H30, and A96082. The alloy and its various tempers are covered by the following standards: [2] EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate.
The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys. To compensate for the lower corrosion resistance, 2219 aluminium can be clad in a commercially pure alloy such as 1050 or painted.
2024-O temper aluminium has no heat treating. It has an ultimate tensile strength of 140–210 MPa (21–30 ksi), and maximum yield strength of no more than 97 MPa (14,000 psi). The material has elongation (stretch before ultimate failure) of 10–25%, this is the allowable range per applicable AMS specifications.
Download as PDF; Printable version; ... 2.6 - 2.8 g/cm3 Shear strength 62 MPa Elastic modulus ... This page was last edited on 21 September 2023, ...
Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
7068 alloy is a 7000 series aluminium-zinc alloy registered with the US Aluminium Association and produced to AMS 4331 (chemical composition and mechanical properties) and AMS 2772 (heat treatment). 7068 alloy ‘A’ and ‘B’ tensile data and fatigue properties have been ratified for inclusion in MIL Handbook 5 / MMPDS.
7055: High-Strength Plate and Extrusion Alloy Microstructure characterization of 7055-T6, 6061-T6511 and 7A52-T6 Al alloys subjected to ballistic impact against heavy tungsten alloy projectile Grain size prediction and investigation of 7055 aluminum alloy inoculated by Al–5Ti–1B master alloy,Journal of Alloys and Compounds - X-MOL