In the nitre bluing process, polished and cleaned steel parts are immersed in a bath of molten salts—typically potassium nitrate and sodium nitrate (sometimes with 9.4 grams (0.33 oz) of manganese dioxide per pound of total nitrate). The mixture is heated to 310 to 321 °C (590 to 610 °F) and the parts are suspended in this solution with wire.
You are free: to share – to copy, distribute and transmit the work; to remix – to adapt the work; Under the following conditions: attribution – You must give appropriate credit, provide a link to the license, and indicate if changes were made.
Niter or nitre [5] is the mineral form of potassium nitrate, KNO 3.It is a soft, white, highly soluble mineral found primarily in arid climates or cave deposits. Historically, the term niter was not well differentiated from natron, both of which have been very vaguely defined but generally refer to compounds of sodium or potassium joined with carbonate or nitrate ions.
Bluing (steel) is a passivation process in which steel is partially protected against rust Bluing may also refer to: Bluing (fabric), a blue dye used to improve the appearance of fabrics; Bluing (hair), a blue dye used to improve the appearance of hair "bluing" of machine parts to check for tolerances, see engineer's blue
Chemical coloring of metals is the process of changing the color of metal surfaces with different chemical solutions. The chemical coloring of metals can be split into three types: electroplating – coating the metal surface with another metal using electrolysis. patination – chemically reacting the metal surface to form a colored oxide or ...
Alchemical symbols were used to denote chemical elements and compounds, as well as alchemical apparatus and processes, until the 18th century. Although notation was partly standardized, style and symbol varied between alchemists.
Engineer's blue is prepared by mixing Prussian blue with a non-drying oily material (for example, grease).The coloured oil is rubbed onto a reference surface, and the workpiece is then rubbed against the coloured reference; the transfer (by contact) of the pigment indicates the position of high spots on the workpiece or conversely highlight low points. [1]
Black oxide is but one type of bluing for firearms; there are other types of bluing used on firearms, too. (Hot bluing vs. cold bluing, and hot bluing versus "hot and cold" mixed bluing, for example.) Black oxide is also used to refer to thicker bluing that is black oxide based.