Stainless steel table with glass plate top. The chairs are polypropylene composite plastic with stainless steel legs. Metal furniture is furniture made with metal parts: iron, carbon steel, aluminium, brass and stainless steel. Iron and steel products are extensively used in many application, ranging from office furnishings to outdoor settings.
A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent grade. 1.4301, the EN 10088 equivalent. [5] 06Cr19Ni10 and ISC S30408, the equivalent in Chinese GB/T 20878 ...
Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an alloy of iron that is resistant to rusting and corrosion. It contains iron with chromium and other elements such as molybdenum , carbon , nickel and nitrogen depending on its specific use and cost.
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]
440C (UNS designation S44004) is a martensitic 400 series stainless steel, [1] and has the highest carbon content of the 400 stainless steel series. It can be heat treated to reach hardness of 58 to 60 HRC. It can be used to make rolling contact stainless bearings, e.g. ball bearings and roller bearings. It is also used to make knife blades.
To qualify as stainless steel, Fe-base alloys must contain at least 10.5%Cr. The iron-chromium phase diagram shows that up to about 13%Cr, the steel undergoes successive transformations upon cooling from the liquid phase from ferritic α phase to austenitic γ phase and back to α.