The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Compressive strength is a limit state of compressive stress that leads to failure in a material in the manner of ductile failure (infinite theoretical yield) or brittle failure (rupture as the result of crack propagation, or sliding along a weak plane – see shear strength). Tensile strength or ultimate tensile strength is a limit state of ...
HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
The ASA mixtures have excellent rutting resistance and moisture damage resistance. The tensile strength ratio of the ASA and asphalt mixture are all larger than 0.8 and therefore satisfy the Superpave specification. The average coefficient of permeability of the ASA mixture is 6–10 times higher than the asphalt mixture in the same air void level.
Inert, thermally stable, tough and high tensile strength: Bottles, pipes, inner insulation (dielectric) of coax cable (see also PTFE), plastic bags, etc. Polypropylene: PP: Resistant to acids and alkalies, High tensile strength: Auto parts, industrial fibers, food containers, liner in bags, dishware and as a wrapping material for textiles and food
The formation of each lamella contributes to the consumption of energy and thus to an increase in elongation at break. Polystyrene homo-polymers deform when a force is applied until they break. Styrene-butane co-polymers do not break at this point, but begin to flow, solidify to tensile strength and only break at much higher elongation. [63]: 426
It has a tensile strength of 85 MPa (12,300 psi) and a Young's modulus of 4,100 MPa (590,000 psi). Its yield strength is 104 ... PAEK plastics are characterized ...
Medium-density polyethylene (MDPE) is a type of polyethylene defined by a density range of 0.926–0.940 g/cm 3. [1] It is less dense than HDPE, which is more common.. MDPE can be produced by chromium/silica catalysts, Ziegler-Natta catalysts or metallocene catalysts.