T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively. [10]
7075 aluminium alloy ... and yield strength of at least 430–480 MPa (63,000–69,000 psi). ... Due to its high strength, low density, thermal properties, and its ...
2024 aluminium alloy is an aluminium alloy, ... Aluminium alloy 2024 has a density of 2.78 g/cm 3 ... and yield strength of at least 270–280 MPa (39–40 ksi). ...
7068-T6511 has typical ultimate tensile strength of 710 MPa (103 ksi) versus a similar product produced from 7075-T6511 that would have a typical ultimate tensile strength of 640 MPa (93 ksi). Typical yield strength for alloy 7068-T6511 is 683 MPa (99.1 ksi) versus 590 MPa (86 ksi) for a similar product produced from 7075-T6511. [2]
Density (ρ) 2.69 g/cm 3 [1] [2] ... AA 6063 is an aluminium alloy, ... (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa ...
Typical material properties for 6060 aluminum alloy include: [2] Density: 2.710 g/cm 3, or 169 lb/ft 3. Young's modulus: 70 GPa, or 10 Msi, or 303 EMEC; Ultimate tensile strength: 140 to 230 MPa, or 20 to 33 ksi. Yield strength: 70 to 180 MPa, or 10 to 26 ksi. Thermal Expansion: 23.4 μm/m-K. Solidus: 610 °C or 1130 °F.
Aluminium 7050 alloy is a heat treatable alloy. It has high toughness, high strength. ... Density 2.6-2.8 g/cm3 Melting point 494°C Tensile strength 515 MPa Yield ...
2090 Aluminium alloy ... Density: 2.59 g/cm 3: Melting point: 560 - 650 °C Mechanical properties. Properties [1] Values Tensile strength: 550 MPa Yield strength: