BHN = load in kilograms divided by the spherical area of the indentation in square millimetres (refer to Brinell scale for method of calculation) It is a rapid, non-destructive (except at the surface being tested) means of determining the hardness of metals. This area is a function of the ball diameter and the depth of the indentation.
A Rockwell hardness tester. The Rockwell hardness test is a hardness test based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
Mechanical testing: hardness testing, tensile testing, Charpy impact testing; Chemical testing: microprobe analysis, energy dispersive spectroscopy; Non-destructive testing: Non-destructive testing is a test method that allows certain physical properties of metal to be examined without taking the samples completely out of service. NDT is ...
The Leeb Rebound Hardness Test (LRHT) invented by Swiss company Proceq SA is one of the four most used methods for testing metal hardness. This portable method is mainly used for testing sufficiently large workpieces (mainly above 1 kg). [citation needed] It measures the coefficient of restitution. It is a form of nondestructive testing.
The Brinell hardness is designated by the most commonly used test standards (ASTM E10-14 [2] and ISO 6506–1:2005) as HBW (H from hardness, B from brinell and W from the material of the indenter, tungsten (wolfram) carbide). In former standards HB or HBS were used to refer to measurements made with steel indenters.
James F. McNulty (U.S. radio engineer) of Automation Industries, Inc., then, in El Segundo, California, an early improver of the many foibles and limits of this and other nondestructive testing methods, teaches in further detail on ultrasonic testing in his U.S. Patent 3,260,105 (application filed December 21, 1962, granted July 12, 1966 ...
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels .