Degraded concrete and rusted, exposed reinforcement bar (rebar) on Welland River bridge of the Queen Elizabeth Way in Niagara Falls, Ontario. Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or
Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
Reinforced concrete is also vulnerable to rust damage. Internal pressure caused by expanding corrosion of concrete-covered steel and iron can cause the concrete to spall, creating severe structural problems. It is one of the most common failure modes of reinforced concrete bridges and buildings.
Bhattacharyya [5] did a study on the three separate types of fungi that are known to cause concrete corrosion: Aspergillus tamarii, Aspergillus niger, and Fusarium. Aspergillus tamarii was the most destructive of the three fungi. It causes cracks to widen and deepen, quickly and efficiently takes root, and promotes calcium oxalate.
Similarly, corrosion of concrete-covered steel and iron can cause the concrete to spall, creating severe structural problems. It is one of the most common failure modes of reinforced concrete bridges. Measuring instruments based on the half-cell potential can detect the potential corrosion spots before total failure of the concrete structure is ...
The effect of sulfuric acid on concrete and steel surfaces exposed to severe wastewater environments can be devastating. [1] In the USA alone, corrosion causes sewer asset losses estimated at $14 billion per year. [2] This cost is expected to increase as the aging infrastructure continues to fail. [3]
Concrete wall cracking as steel reinforcing corrodes and swells. Rust has a lower density than metal, so it expands as it forms, cracking the decorative cladding off the wall as well as damaging the structural concrete. The breakage of material from a surface is called spalling.
The initiation time is related to the rate at which carbonation propagates in the concrete cover thickness.Once that carbonation reaches the steel surface, altering the local pH value of the environment, the protective thin film of oxides on the steel surface becomes instable, and corrosion initiates involving an extended portion of the steel surface.