Calcium hydroxide is moderately soluble in water, as seen for many dihydroxides. Its solubility increases from 0.66 g/L at 100 °C to 1.89 g/L at 0 °C. [8] Its solubility product K sp of 5.02 × 10 −6 at 25 °C, [1] its dissociation in water is large enough that its solutions are basic according to the following dissolution reaction:
The following chart shows the solubility of various ionic compounds in water at 1 atm pressure and room temperature (approx. 25 °C, 298.15 K). "Soluble" means the ionic compound doesn't precipitate, while "slightly soluble" and "insoluble" mean that a solid will precipitate; "slightly soluble" compounds like calcium sulfate may require heat to precipitate.
CaO + H 2 O → Ca(OH) 2 Ca(OH) 2 + CO 2 → CaCO 3 + H 2 O. In a laboratory, calcium carbonate can easily be crystallized from calcium chloride (CaCl 2), by placing an aqueous solution of CaCl 2 in a desiccator alongside ammonium carbonate [NH 4] 2 CO 3. [10] In the desiccator, ammonium carbonate is exposed to air and decomposes into ammonia ...
Carbonatation is a slow process that occurs in concrete where lime (CaO, or Ca(OH) 2 ) in the cement reacts with carbon dioxide (CO 2) from the air and forms calcium carbonate. The water in the pores of Portland cement concrete is normally alkaline with a pH in the range of 12.5 to 13.5.
Calcium oxide (formula: Ca O), commonly known as quicklime or burnt lime, is a widely used chemical compound. It is a white, caustic , alkaline , crystalline solid at room temperature . The broadly used term lime connotes calcium-containing inorganic compounds , in which carbonates , oxides , and hydroxides of calcium, silicon , magnesium ...
Ca(OH) 2 or CaO · H 2 O: Calcium hydroxide (portlandite) C-S-H: 0.6–2.0 CaO · SiO 2 · 0.9–2.5 H 2 O, with variable composition within this range, and often also incorporating partial substitution of Al for Si: Calcium silicate hydrate: C-A-H: Phase more complex than C-S-H: Calcium aluminate hydrate C-A-S-H: This is even more complex than ...