Stress–strain curve for brittle materials compared to ductile materials. Some common characteristics among the stress–strain curves can be distinguished with various groups of materials and, on this basis, to divide materials into two broad categories; namely, the ductile materials and the brittle materials. [1]: 51
In this form, K and n are not the same as the constants commonly seen in the Hollomon equation. [2] The equation is essentially assuming the elastic strain portion of the stress-strain curve, , can be modeled with a line, while the plastic portion, , can be modeled with a power law. The elastic and plastic components are summed to find the ...
In fracture mechanics, the stress intensity factor (K) is used to predict the stress state ("stress intensity") near the tip of a crack or notch caused by a remote load or residual stresses. [1] It is a theoretical construct usually applied to a homogeneous, linear elastic material and is useful for providing a failure criterion for brittle ...
Other models may also include the effects of strain gradients. [3] Independent of test conditions, the flow stress is also affected by: chemical composition, purity, crystal structure, phase constitution, microstructure, grain size, and prior strain. [4] The flow stress is an important parameter in the fatigue failure of ductile materials.
Fig. 1: Critical stress vs slenderness ratio for steel, for E = 200 GPa, yield strength = 240 MPa. Euler's critical load or Euler's buckling load is the compressive load at which a slender column will suddenly bend or buckle. It is given by the formula: [1] = where
The point in the stress-strain curve at which the curve levels off and plastic deformation begins to occur. [13] Offset yield point (proof stress) When a yield point is not easily defined on the basis of the shape of the stress-strain curve an offset yield point is arbitrarily defined.
The strain hardening exponent (also called the strain hardening index), usually denoted , is a measured parameter that quantifies the ability of a material to become stronger due to strain hardening. Strain hardening (work hardening) is the process by which a material's load-bearing capacity increases during plastic (permanent) strain , or ...
This is not true since the actual area will decrease while deforming due to elastic and plastic deformation. The curve based on the original cross-section and gauge length is called the engineering stress–strain curve, while the curve based on the instantaneous cross-section area and length is called the true stress–strain curve. Unless ...