Each alloy is given a four-digit number, where the first digit indicates the major alloying elements, the second — if different from 0 — indicates a variation of the alloy, and the third and fourth digits identify the specific alloy in the series. For example, in alloy 3105, the number 3 indicates the alloy is in the manganese series, 1 ...
2 Mechanical Properties. ... 5 Aluminum alloy table. Toggle the table of contents. 1200 aluminium alloy. ... 1200 Aluminium alloy has aluminium as the major element, ...
2218 aluminium alloy is an alloy in the wrought aluminium-copper family (2000 or 2xxx series). It is one of the most complex grades in the 2000 series, with at least 88.4% aluminium by weight. Unlike most other aluminium-copper alloys, 2218 is a high work-ability alloy, with relatively low for 2xxx series alloy yield strength of 255 MPa.
Aluminium alloys are alloys where the principal metal is aluminium. Subcategories. This category has the following 7 subcategories, out of 7 total. ...
Aluminium-silicon alloys typically contain 3% to 25% silicon content. [1] Casting is the primary use of aluminum-silicon alloys, but they can also be utilized in rapid solidification processes and powder metallurgy. Alloys used by powder metallurgy, rather than casting, may contain even more silicon, up to 50%. [1]
4 Aluminium alloy table. 5 References. ... 2017 Aluminium alloy has copper, iron, magnesium, ... Thermal Properties [2] Values CTE, linear 68°F ...
2219 aluminium alloy is an alloy in the wrought aluminium-copper family (2000 or 2xxx series). It can be heat-treated to produce tempers with higher strength but lower ductility. The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys.
The name is mainly used in pop-science to describe all Al-Cu alloys system. Aluminium–copper alloys were standardised in the 2000 series by the international alloy designation system (IADS) which was originally created in 1970 by the Aluminum Association. 2000s series includes 2014 and 2024 alloys used in airframe fabrication.