Chrome plating (less commonly chromium plating) is a technique of electroplating a thin layer of chromium onto a metal object. A chrome plated part is called chrome , or is said to have been chromed .
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
A standard black oxide is magnetite (Fe 3 O 4), which is more mechanically stable on the surface and provides better corrosion protection than red oxide Fe 2 O 3. Modern industrial approaches to forming black oxide include the hot and mid-temperature processes described below. Traditional methods are described in the article on bluing. They are ...
The protective effect of chromate coatings on zinc is indicated by color, progressing from clear/blue to yellow, gold, olive drab and black. Darker coatings generally provide more corrosion resistance. [11] The coating color can also be changed with dyes, so color is not a complete indicator of the process used.
Plating is a finishing process in which a metal is deposited on a surface. Plating has been done for hundreds of years; it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve solderability, to harden, to improve wearability, to reduce friction, to improve paint adhesion, to alter conductivity, to improve IR reflectivity, for ...
The process is slow, so more efficient plating processes are used once the desired strike thickness is obtained. The striking method is also used in combination with the plating of different metals. If it is desirable to plate one type of deposit onto a metal to improve corrosion resistance but this metal has inherently poor adhesion to the ...
Similar processes can be found on some ancient Egyptian copper sheets. [3] Another example of early chemical coloring of metals is the Nebra sky disk, which has a green patina and gold inlays. An early example of black colored iron is the famous Celtic spearhead found in the River Thames and dated between 200 and 50 BC. [4] [5]
Electropolishing, also known as electrochemical polishing, anodic polishing, or electrolytic polishing (especially in the metallography field), is an electrochemical process that removes material from a metallic workpiece, reducing the surface roughness by levelling micro-peaks and valleys, improving the surface finish.