Depending on the holding temperature, austempering can produce either upper or lower bainite. Upper bainite is a laminate structure formed at temperatures typically above 350 °C (662 °F) and is a much tougher microstructure.
The most notable difference between austempering and conventional quench and tempering is that it involves holding the workpiece at the quenching temperature for an extended period of time. The basic steps are the same whether applied to cast iron or steel and are as follows:
[2] [6] The specified holding temperature is one that is at a high enough temperature to relieve high residual stress levels, yet is still below the lower transformation temperature. [ 1 ] [ 2 ] In addition to the reduction of stress, high hold temperatures below the transformation temperature allow for microstructural transformations, therein ...
Proper heat treating requires precise control over temperature, time held at a certain temperature and cooling rate. [ 12 ] With the exception of stress-relieving, tempering, and aging, most heat treatments begin by heating an alloy beyond a certain transformation, or arrest (A), temperature.
The temperature range for process annealing ranges from 260 °C (500 °F) to 760 °C (1400 °F), depending on the alloy in question. This process is mainly suited for low-carbon steel. The material is heated up to a temperature just below the lower critical temperature of steel.
For premium support please call: 800-290-4726 more ways to reach us
A complete cycle involves heating the oven to the required temperature, maintaining that temperature for the proper time interval for that temperature, turning the machine off and cooling the articles in the closed oven till they reach room temperature. The standard settings for a hot air oven are: 1.5 to 2 hours at 160 °C (320 °F)
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!