Cast iron is made from pig iron, which is the product of melting iron ore in a blast furnace. Cast iron can be made directly from the molten pig iron or by re-melting pig iron, [4] often along with substantial quantities of iron, steel, limestone, carbon (coke) and taking various steps to remove undesirable contaminants.
Main page; Contents; Current events; Random article; About Wikipedia; Contact us; Donate
Gray iron, or grey cast iron, is a type of cast iron that has a graphitic microstructure. It is named after the gray color of the fracture it forms, which is due to the presence of graphite. [ 1 ] It is the most common cast iron and the most widely used cast material based on weight.
Cast iron is a brittle form of iron which is weaker in tension than in compression. It has a relatively low melting point, good fluidity, castability, excellent machinability and wear resistance. Though almost entirely replaced by steel in building structures, cast irons have become an engineering material with a wide range of applications ...
Wrought iron is an iron alloy with a very low carbon content (less than 0.05%) in contrast to that of cast iron (2.1% to 4.5%). It is a semi-fused mass of iron with fibrous slag inclusions (up to 2% by weight), which give it a wood-like "grain" that is visible when it is etched, rusted, or bent to failure.
Ductile iron is used in many piano harps (the iron plates which anchor piano strings). Ductile iron is used for vises. Previously, regular cast iron or steel was commonly used. The properties of ductile iron make it a significant upgrade in strength and durability from cast iron without having to use steel, which is expensive and has poor ...
Meehanite is a trademark for an engineering process to make a range of cast irons produced under specific and carefully controlled conditions to precise internationally recognized specifications. According to the Meehanite Worldwide company, when correctly followed the Meehanite process will produce cast iron with uniform soundness, consistent ...
Ductile iron pipe is different than cast iron, because the introduction of magnesium during the casting process causes the graphite to form spheres (graphite nodules) rather than flakes. While this allows the material to remain castable, the end product is much tougher than cast iron, and allows elastic behavior at lower stress levels. [1]