Typical lectromechanical Universal Testing Machine Test fixture for three point flex test. A universal testing machine (UTM), also known as a universal tester, [1] universal tensile machine, materials testing machine, materials test frame, is used to test the tensile strength (pulling) and compressive strength (pushing), flexural strength, bending, shear, hardness, and torsion testing ...
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
Shore durometer hardness, used for polymers; Barcol hardness test, for composite materials; Tensile testing, used to obtain the stress-strain curve for a material, and from there, properties such as Young modulus, yield (or proof) stress, tensile stress and % elongation to failure. Impact testing Izod test; Charpy test; Fracture toughness testing
The punch is then pushed with a constant displacement rate through the specimen. A flat punch or concave tip pushing a ball are typically used in the test. [24] After the testing, some characteristic parameters such as force-displacement curves are used to estimate yield strength, ultimate tensile stress.
Creep machines are used to understand the creep of materials and determine which type can do the job better, which is important when making and designing materials for everyday uses. They most commonly test the creep of alloys and plastics for the understanding of their properties and advantages of one material's use over another. [2]
The ultimate strength is the maximum stress that a material can withstand before it breaks or weakens. [12] For example, the ultimate tensile strength (UTS) of AISI 1018 Steel is 440 MPa. In Imperial units, the unit of stress is given as lbf/in 2 or pounds-force per square inch. This unit is often abbreviated as psi.
The results from the test are commonly used to select a material for an application, for quality control, or to predict how a material will react under other types of forces. Properties that are directly measured via a tensile test are the ultimate tensile strength, maximum elongation and reduction in cross-section area.