Rosin used as flux for soldering A flux pen used for electronics rework Multicore solder containing flux Wire freshly coated with solder, held above molten rosin flux. In metallurgy, a flux is a chemical reducing agent, flowing agent, or purifying agent. Fluxes may have more than one function at a time.
Solderability when using lead-free alloys can differ significantly from solderability when using lead based alloys. Noble metals may be easy to solder but they have brittle joints. The metals in the good category require a large amount of heat therefore oxidation is an issue. To overcome this a flux is required.
A silversmith hard soldering of silver rings using flux and silver solder wire. "Hard soldering" or "silver soldering" is used to join precious and semi-precious metals such as gold, silver, brass, and copper. The solder is usually described as easy, medium, or hard in reference to its melting temperature, not the strength of the joint.
Reflow soldering is a process in which a solder paste (a sticky mixture of powdered solder and flux) is used to temporarily attach anywhere from one to thousands of tiny electrical components to their contact pads, after which the entire assembly is subjected to controlled heat. The solder paste reflows in a molten state, creating permanent ...
In industry, rosin is a flux used in soldering. The lead-tin solder commonly used in electronics has 1 to 2% rosin by weight as a flux core, helping the molten metal flow and making a better connection by reducing the refractory solid oxide layer formed at the surface back to metal. It is frequently seen as a burnt or clear residue around new ...
A wet small sponge, often supplied with soldering equipment, can be used to wipe the tip. For lead-free solder a slightly more aggressive cleaning, with brass shavings, can be used. Soldering flux will help to remove oxide; the more active the flux the better the cleaning, although acidic flux used on circuit boards that is not carefully ...
The paste manufacturer will suggest a suitable reflow temperature profile to suit their individual paste. The main requirement is a gentle rise in temperature to prevent explosive expansion (which can cause "solder balling"), yet activate the flux. Thereafter, the solder melts. The time in this area is known as Time Above Liquidus. A reasonably ...
Flux in the wave soldering process has a primary and a secondary objective. The primary objective is to clean the components that are to be soldered, principally any oxide layers that may have formed. [3] There are two types of flux, corrosive and noncorrosive. Noncorrosive flux requires precleaning and is used when low acidity is required.