The ASA mixtures have excellent rutting resistance and moisture damage resistance. The tensile strength ratio of the ASA and asphalt mixture are all larger than 0.8 and therefore satisfy the Superpave specification. The average coefficient of permeability of the ASA mixture is 6–10 times higher than the asphalt mixture in the same air void level.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Compressive strength is a limit state of compressive stress that leads to failure in a material in the manner of ductile failure (infinite theoretical yield) or brittle failure (rupture as the result of crack propagation, or sliding along a weak plane – see shear strength). Tensile strength or ultimate tensile strength is a limit state of ...
Inert, thermally stable, tough and high tensile strength: Bottles, pipes, inner insulation (dielectric) of coax cable (see also PTFE), plastic bags, etc. Polypropylene: PP: Resistant to acids and alkalies, High tensile strength: Auto parts, industrial fibers, food containers, liner in bags, dishware and as a wrapping material for textiles and food
HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
Tensile strength (σ t) 50–80 M Pa: Elongation (ε) at break: 20–40%: Notch test: 2–5 k J/m 2: Thermal properties; Melting temperature (T m) 150 °C [citation needed] Glass transition temperature (T g) 106–115 °C: Vicat softening point—50 N (Vicat B) 106–115 °C: Thermal conductivity (k) 0.16 W/(m·K) Linear thermal expansion ...
Tensile strength, ultimate ASTM D 638 MPa, average value 91.6 Tensile modulus ASTM D 638 GPa, average value 3.97 Tensile elongation ASTM D 638 % 3.15 Flexural strength ASTM D 790 MPa 133 Flexural modulus ASTM D 638 GPa 4.58 Compressive strength ASTM D 695 MPa, average 132 Izod impact strength ASTM D 256 J/m (ft-lb/in) average 0.521 (1)
Ductility: Ability of a material to deform under tensile load (% elongation). It is the property of a material by which it can be drawn into wires under the action of tensile force. A ductile material must have a high degree of plasticity and strength so that large deformations can take place without failure or rupture of the material.