Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength , breaking strength , maximum elongation and reduction in area. [ 2 ]
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
Values for the flexural strength measured with four-point bending will be significantly lower than with three-point bending., [7] Compared with three-point bending test, this method is more suitable for strength evaluation of butt joint specimens. The advantage of four-point bending test is that a larger portion of the specimen between two ...
This test is performed on a universal testing machine (tensile testing machine or tensile tester) with a three-point or four-point bend fixture. The main advantage of a three-point flexural test is the ease of the specimen preparation and testing.
Properties that are directly measured via a tensile test are the ultimate tensile strength, maximum elongation and reduction in cross-section area. From these measurements, properties such as Young's modulus, Poisson's ratio, yield strength, and the strain-hardening characteristics of the sample can be determined.
It is a generalized form of tensile testing in which the material sample is simultaneously stressed along two perpendicular axes. Typical materials tested in biaxial configuration include metal sheets , [ 1 ] silicone elastomers , [ 2 ] composites , [ 3 ] thin films , [ 4 ] textiles [ 5 ] and biological soft tissues .
Typical lectromechanical Universal Testing Machine Test fixture for three point flex test. A universal testing machine (UTM), also known as a universal tester, [1] universal tensile machine, materials testing machine, materials test frame, is used to test the tensile strength (pulling) and compressive strength (pushing), flexural strength, bending, shear, hardness, and torsion testing ...
time to specimen failure (e.g., breakage, or from other "failure" criteria) ductility (by elongation to fracture or the reduction of the area) ultimate tensile strength (from the maximum load) area under the elongation - load curve (which represents the fracture energy) percent of ductile/brittle fracture on the fracture surface