Stainless steel, also known as inox, corrosion-resistant steel (CRES), and rustless steel, is an iron-based alloy containing a minimum level of chromium that is resistant to rusting and corrosion. Stainless steel's resistance to corrosion results from the 10.5%, or more, chromium content which forms a passive film that can protect the material ...
A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent grade. 1.4301, the EN 10088 equivalent. [5] 06Cr19Ni10 and ISC S30408, the equivalent in Chinese GB/T 20878 ...
It is also known as the strength-to-weight ratio or strength/weight ratio or strength-to-mass ratio. In fiber or textile applications, tenacity is the usual measure of specific strength. The SI unit for specific strength is Pa ⋅ m 3 / kg , or N ⋅m/kg, which is dimensionally equivalent to m 2 /s 2 , though the latter form is rarely used.
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
The noun steel originates from the Proto-Germanic adjective *stahliją or *stakhlijan 'made of steel', which is related to *stahlaz or *stahliją 'standing firm'. [4] The carbon content of steel is between 0.02% and 2.14% by weight for plain carbon steel (iron-carbon alloys). Too little carbon content leaves (pure) iron quite soft, ductile, and ...
Carbon steels and alloy steels are designated a four digit number, whereby the first digit indicates the main alloying element(s), the second digit indicates tg (top grade) element(s), and the last two digits indicate the amount of carbon, in hundredths of a percent (basis points) by weight. For example, a 1060 steel is a plain-carbon steel ...
SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...