An ingot is a piece of relatively pure material, usually metal, that is cast into a shape suitable for further processing. [1] In steelmaking, it is the first step among semi-finished casting products. Ingots usually require a second procedure of shaping, such as cold/hot working, cutting, or milling to produce a useful final product.
In the era of commercial wrought iron, blooms were slag-riddled iron castings poured in a bloomery before being worked into wrought iron. In the era of commercial steel, blooms are intermediate-stage pieces of steel produced by a first pass of rolling (in a blooming mill) that works the ingots down to a smaller cross-sectional area, but still greater than 36 in 2 (230 cm 2). [1]
Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills. Prior to the introduction of continuous casting in the 1950s, steel was poured into stationary molds to form ingots. Since then, "continuous casting" has ...
Die casting – Metal mold. Billet (ingot) casting – Simple mold for producing ingots of metal, normally for use in other foundries. Loam molding – a built up mold used for casting large objects, such as cannon, steam engine cylinders, and bells.
It is also used for any steel castings. [6] Note that decrease in carbon content increases the problems with non-metallic inclusions. [7] [needs update] Continuous casting and strip-casting technologies have largely superseded ingot casting techniques in recent times. Through these methods, all steel is killed and the resulting yields are close ...
Molten metal before casting Casting iron in a sand mold. In metalworking and jewelry making, casting is a process in which a liquid metal is delivered into a mold (usually by a crucible) that contains a negative impression (i.e., a three-dimensional negative image) of the intended shape.
Today, approximately 96% of steel is continuously cast, while only 4% is produced as ingots. [16] The ingots are then heated in a soaking pit and hot rolled into slabs, billets, or blooms. Slabs are hot or cold rolled into sheet metal or plates. Billets are hot or cold rolled into bars, rods, and wire.
Direct Chill casting is a method for the fabrication of cylindrical or rectangular solid ingots from non-ferrous metals, especially Aluminum, Copper, Magnesium and their alloys. The original ingots are usually further processed by other methods (rolling, forging, etc.). More than half of global aluminum production uses the Direct Chill casting ...