It is suggested that these lesions are caused by forces placed on the teeth during biting, eating, chewing and grinding; the enamel, especially at the cementoenamel junction (CEJ), undergoes large amounts of stress, causing micro fractures and tooth tissue loss. Abfraction appears to be a modern condition, with examples of non-carious cervical ...
This type of stress may be called (simple) normal stress or uniaxial stress; specifically, (uniaxial, simple, etc.) tensile stress. [13] If the load is compression on the bar, rather than stretching it, the analysis is the same except that the force F and the stress σ {\displaystyle \sigma } change sign, and the stress is called compressive ...
Tensile stress forms joints in rocks. A joint is a fracture that forms within a rock, whose movement to open the fracture is greater than the lateral movement that takes place. Joints are formed in the direction perpendicular to the least principal stress, meaning that they are formed perpendicular to the tensile stress. [ 1 ]
Tensile strength or ultimate tensile strength is a limit state of tensile stress that leads to tensile failure in the manner of ductile failure (yield as the first stage of that failure, some hardening in the second stage and breakage after a possible "neck" formation) or brittle failure (sudden breaking in two or more pieces at a low-stress ...
[1]: 58 For example, low-carbon steel generally exhibits a very linear stress–strain relationship up to a well-defined yield point. The linear portion of the curve is the elastic region, and the slope of this region is the modulus of elasticity or Young's modulus. Plastic flow initiates at the upper yield point and continues at the lower ...
As for the tensile strength point, it is the maximal point in engineering stress–strain curve but is not a special point in true stress–strain curve. Because engineering stress is proportional to the force applied along the sample, the criterion for necking formation can be set as δ F = 0. {\displaystyle \delta F=0.}
When an external tensile stress is applied to the material, the crack tips concentrate stress, increasing the local tensile stresses experienced at the crack tips to a greater extent than the average stress on the bulk material. This causes the initial crack to enlarge quickly (propagate) as the surrounding material is overwhelmed by the stress ...
In everyday life, compressive stresses are common in many structures and materials. For instance, the weight of a building creates compressive stresses in its walls and foundations. Similarly, when a person stands, the bones in their legs experience compressive stresses due to the weight of the body pushing down.