The AlMgSi alloys are therefore understood in the standards as a separate group (6000 series) and not as a subgroup of aluminum-magnesium alloys that cannot be hardenable. AlMgSi is one of the aluminum alloys with medium to high strength, high fracture resistance, good welding suitability, corrosion resistance and formability. They can be ...
AlSi10Mg-0403 alloy is a specific type of AlSi10Mg that comprises aluminium alloyed with silicon of mass fraction up to 10%, small quantities of magnesium and iron, along with other minor elements. The presence of silicon makes the alloy both harder and stronger than pure aluminium due to the formation of Mg 2 Si precipitate.
Aluminum-silicon phase diagram. Aluminum forms a eutectic with silicon, which is at 577 °C, with a Si content of 12.5% [7] or 12.6%. [8] Up to 1.65% Si can be dissolved in aluminum at this temperature. However, the solubility decreases rapidly with temperature. At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si.
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
Alusil as a hypereutectic aluminium-silicon alloy (EN AC-AlSi17Cu4Mg / EN AC-48100 or A390) contains approximately 78% aluminium and 17% silicon. [1] [2] This alloy was theoretically conceived in 1927 by Schweizer & Fehrenbach, [3] of Badener Metall-Waren-Fabrik, [4] but practically created only by Lancia [5] in the same year, for its car engines.
0–9. 1050 aluminium alloy; 1060 aluminium alloy; 1070 aluminium alloy; 1100 aluminium alloy; 1145 aluminium alloy; 1199 aluminium alloy; 1200 aluminium alloy
Aluminized steel can be made using a variety of processes, cladding, hot dipping, galvanic coating, metallizing, and calorizing, but the most effective process is hot dipping. The process of hot dipping starts by cleaning the steel, then placing the steel in a bath of Al-11%Si at a temperature of 988K and shaken, then pulled out and air dried. [5]
Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel.