Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi). More typical values are 310 MPa (45 ksi) and 270 MPa (39 ksi), respectively. [ 10 ]
The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys. To compensate for the lower corrosion resistance, 2219 aluminium can be clad in a commercially pure alloy such as 1050 or painted.
Heat treatment can improve its anti-corrosion properties with a low corresponding decrease in strength. [1 ... Ultimate tensile strength [3 ... of_7150_aluminum_alloy ...
Tensile Strength, Ultimate: 83.0 MPa Tensile Strength, Yield: 28.0 MPa Elongation at Break: 28 % Modulus of Elasticity: 68.9 GPa Electrical Resistivity: 0.00000280 ohm-cm
The most common forming method is extrusion. It can also be forged or rolled, but as a wrought alloy it is not used in casting. It is commonly heat treated to produce tempers with a higher strength at the expense of ductility. [1] Alternate names and designations include AlSiMg and A96005.
It cannot be work hardened, but is commonly heat treated to produce tempers with a higher strength but lower ductility. [1] Alternate names and designations include AlSi1MgMn, 3.2315, H30, and A96082. The alloy and its various tempers are covered by the following standards: [2] EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate.
Typical applications include marine, aircraft, architecture, general sheet metal work, heat exchangers, fuel lines and tanks, flooring panels, streetlights, appliances, rivets and wire. The exceptional corrosion resistance of 5052 alloy against seawater and salt spray makes it a primary candidate for the failure-sensitive large marine ...