Direct reduced iron (DRI), also called sponge iron, [1] is produced from the direct reduction of iron ore (in the form of lumps, pellets, or fines) into iron by a reducing gas which contains elemental carbon (produced from natural gas or coal) and/or hydrogen. When hydrogen is used as the reducing gas no carbon dioxide is produced.
In the iron and steel industry, direct reduction is a set of processes for obtaining iron from iron ore, by reducing iron oxides without melting the metal. The resulting product is pre-reduced iron ore. Historically, direct reduction was used to obtain a mix of iron and slag called a bloom in a bloomery.
The HIsarna ironmaking process is a direct reduced iron process for iron making in which iron ore is processed almost directly into liquid iron ().The process combines two process units, the Cyclone Converter Furnace (CCF) for ore melting and pre-reduction and a Smelting Reduction Vessel (SRV) where the final reduction stage to liquid iron takes place.
Iron powder is formed as a whole from several other iron particles. The particle sizes vary anywhere from 20-200 μm. The iron properties differ depending on the production method and history of a specific iron powder. There are three types of iron powder classifications: reduced iron powder, atomized powder, [2] and electrolytic iron powder ...
Elemental iron, or reduced iron, despite being absorbed at only one-third to two-thirds the efficiency (relative to iron sulfate), [165] is often added to foods such as breakfast cereals or enriched wheat flour. Iron is most available to the body when chelated to amino acids [166] and is also available for use as a common iron supplement.
Iron oxide becomes metallic iron at roughly 1250 °C (2282 °F or 1523 K), almost 300 degrees below iron's melting point of 1538 °C (2800 °F or 1811 K). [ 5 ] Mercuric oxide becomes vaporous mercury near 550 °C (1022 °F or 823 K), almost 600 degrees above mercury's melting point of -38 °C (-36.4 °F or 235 K), and also above mercury's ...
Iron treated this way is said to be wrought (worked), and the resulting iron, with reduced amounts of slag, is called wrought iron or bar iron. Because of the creation process, individual blooms can often have differing carbon contents between the original top and bottom surfaces, differences that will also be somewhat blended together through ...