Direct reduced iron (DRI), also called sponge iron, [1] is produced from the direct reduction of iron ore (in the form of lumps, pellets, or fines) into iron by a reducing gas which contains elemental carbon (produced from natural gas or coal) and/or hydrogen. When hydrogen is used as the reducing gas no carbon dioxide is produced.
Pre-reduced iron ore briquettes. Packaging of pre-reduced iron ore is evenly divided between sponge iron and briquettes. Sponges are a highly porous metallic product, close to the original ore but highly pyrophoric, which limits their transport. They are therefore often subjected to hot compaction, which improves both product density and ...
Elemental iron is virtually absent on the Earth's surface except as iron-nickel alloys from meteorites and very rare forms of deep mantle xenoliths.Although iron is the fourth most abundant element in Earth's crust, composing about 5% by weight, [4] the vast majority is bound in silicate or, more rarely, carbonate minerals, and smelting pure iron from these minerals would require a prohibitive ...
The HIsarna ironmaking process is a direct reduced iron process for iron making in which iron ore is processed almost directly into liquid iron ().The process combines two process units, the Cyclone Converter Furnace (CCF) for ore melting and pre-reduction and a Smelting Reduction Vessel (SRV) where the final reduction stage to liquid iron takes place.
Iron powder is formed as a whole from several other iron particles. The particle sizes vary anywhere from 20-200 μm. The iron properties differ depending on the production method and history of a specific iron powder. There are three types of iron powder classifications: reduced iron powder, atomized powder, [2] and electrolytic iron powder ...
Material hardening is required for many applications: Machine cutting tools (drill bits, taps, lathe tools) need be much harder than the material they are operating on in order to be effective. Knife blades – a high hardness blade keeps a sharp edge. Bearings – necessary to have a very hard surface that will withstand continued stresses.
Cast iron comes in many types, depending on the carbon content. However, they are usually divided into grey and white cast iron, depending on the form that the carbides take. In grey cast iron, the carbon is mainly in the form of graphite, but in white cast iron, the carbon is usually in the form of cementite.
Low-pressure phase diagram of pure iron. BCC is body centered cubic and FCC is face-centered cubic. Iron-carbon eutectic phase diagram, showing various forms of Fe x C y substances. Iron allotropes, showing the differences in structure. The alpha iron (α-Fe) is a body-centered cubic (BCC) and the gamma iron (γ-Fe) is a face-centered cubic (FCC).