It cannot be work hardened, but is commonly heat treated to produce tempers with a higher strength but lower ductility. [1] Alternate names and designations include AlSi1MgMn, 3.2315, H30, and A96082. The alloy and its various tempers are covered by the following standards: [2] EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate.
The peak yield strength is also dependent on percent aluminum in the FeAl alloy. As the percent aluminum increases, the peak yield strength occurs at lower temperatures. [8] The yield strength anomaly in FeAl alloys can be hidden if thermal vacancies are not minimized through a slow anneal at a relatively low temperature (~400 °C for ~5 days ...
Most strength is recovered in the first few days to a few weeks. Nevertheless, the Aluminum Design Manual (Aluminum Association) recommends the design strength of the material adjacent to the weld to be taken as 165 MPa/24000 PSI without proper heat treatment after the welding. Typical filler material is 4043 or 5356.
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
Table of Refractive index; Wavelength(μm): n o: n e: 0.193: 1.92879: 1.91743 0.213: 1.88903: 1.87839 0.222: 1.8754: 1.86504 0.226: 1.87017: 1.85991 0.244: 1.85059: 1 ...
6060 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is much more closely related to the alloy 6063 than to 6061.The main difference between 6060 and 6063 is that 6063 has a slightly higher magnesium content.
5154 aluminium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). As an aluminium-magnesium alloy, it combines moderate-to-high strength with excellent weldability. 5154 aluminium is commonly used in welded structures such as pressure vessels and ships.