The Electrochemical Fatigue Crack Sensor. In 1992, Dr. Campbell Laird and Dr. Yuanfeng Li invented the EFS™. The EFS™ relies on a patented electrical test [2] [3] method, which monitors the current flow at the surface of a metal while it is being mechanically flexed. The output current resembles a heart’s EKG pattern and can be ...
Scanning electron microscope image of fatigue striations produced from constant amplitude loading. The crack is growing from left to right. Striations are marks produced on the fracture surface that show the incremental growth of a fatigue crack. A striation marks the position of the crack tip at the time it was made.
White etching cracks (WEC), or white structure flaking or brittle flaking, is a type of rolling contact fatigue (RCF) damage that can occur in bearing steels under certain conditions, such as hydrogen embrittlement, high stress, inadequate lubrication, and high temperature. WEC is characterised by the presence of white areas of microstructural ...
The oil and whiting method used in the railroad industry in the early 1900s was the first recognized use of the principles of penetrants to detect cracks. The oil and whiting method used an oil solvent for cleaning followed by the application of a whiting or chalk coating, which absorbed oil from the cracks revealing their locations.
It is the result of the process of fatigue due to rolling/sliding contact. [2] [3] The RCF process begins with cyclic loading of the material, which results in fatigue damage that can be observed in crack-like flaws, like white etching cracks. [2] These flaws can grow into larger cracks under further loading, potentially leading to fractures ...
In true corrosion fatigue, the fatigue-crack-growth rate is enhanced by corrosion; this effect is seen in all three regions of the fatigue-crack growth-rate diagram. The diagram on the left is a schematic of crack-growth rate under true corrosion fatigue; the curve shifts to a lower stress-intensity-factor range in the corrosive environment.
Demonstration of tested specimen and IRNDT analysis results. IRNDT (infra-red nondestructive testing) method is suitable for detection and inspection of cracks, defects, cavities, voids and inhomogeneities in material, it is also possible to use the method for inspection of welded joints of metal and plastic parts, inspection of solar cells and solar panels, determination of internal structure ...
The technique is very sensitive and can detect tight cracks. Surface inspection can be performed both on ferromagnetic and non-ferromagnetic materials. [8] [9] Tubing inspection is generally limited to non-ferromagnetic tubing and is known as conventional eddy current testing.