Pearlite is a two-phased, lamellar (or layered) structure composed of alternating layers of ferrite (87.5 wt%) and cementite (12.5 wt%) that occurs in some steels and cast irons. During slow cooling of an iron-carbon alloy, pearlite forms by a eutectoid reaction as austenite cools below 723 °C (1,333 °F) (the eutectoid temperature).
When using the chart, it is important to remember these tips: Isotropic and opaque (metallic) minerals cannot be identified this way. The stage of the microscope should be rotated until maximum colour is found, and therefore, the maximum birefringence. Each mineral, depending on the orientation, may not exhibit the maximum birefringence.
[2] [3] Acicular ferrite is a fine Widmanstätten constituent, which is nucleated by an optimum intragranular dispersion of oxide/sulfide/silicate particles. The interlocking nature of acicular ferrite, together with its fine grain size (0.5 to 5 μm with aspect ratio from 3:1 to 10:1), provides maximum resistance to crack propagation by cleavage.
As a result of the transformation, the microconstituents, pearlite and bainite, form; pearlite forms at higher temperatures and bainite at lower. TTT diagram of isothermal transformations of a hypoeutectoid carbon steel; showing the main components obtained when cooling the steel and its relation with the Fe-C phase diagram of carbon steels.
This increases the brittleness of the steel in a way that can only be relieved by recrystallizing. Widmanstätten structures made from ferrite sometimes occur in carbon steel, if the carbon content is below but near the eutectoid composition (~ 0.8% carbon). This occurs as long needles of ferrite within the pearlite. [16]
It looks like Aurora Borealis shooting over a mountain range, but it's not.. This is a photograph of a gemstone taken under a microscope. If you're thinking, "I could look at these breath taking ...
A very rapid quench is essential to create martensite. For a eutectoid carbon steel of thin section, if the quench starting at 750 °C and ending at 450 °C takes place in 0.7 seconds (a rate of 430 °C/s) no pearlite will form, and the steel will be martensitic with small amounts of retained austenite. [2]
Under a light microscope, the microstructure of bainite appears darker than untempered martensite because the bainite has more substructure. [9] The hardness of bainite can be between that of pearlite and untempered martensite in the same steel hardness. The fact that it can be produced during both isothermal or continuous cooling is a big ...