Reactive hot isostatic pressing (hipping) at ≈40 MPa of the appropriate mixtures of Ti, Al 4 C 3 graphite, for 15 hours at 1300 °C yields predominantly single-phase samples of Ti 2 AlC 0.5 N 0.5, 30 hours at 1300 °C yields predominantly single-phase samples of Ti 2 AlC (Titanium aluminium carbide).
The HIP process subjects a component to both elevated temperature and isostatic gas pressure within a high-pressure containment vessel, unlike the cold isostatic pressing (CIP), where the component is maintained at room temperature. [2] The pressurizing gas most widely used is argon. An inert gas is used so that the material does not chemically ...
In this type of process metallic chromium and pure carbon in the form of graphite are loaded into a ball mill and ground into a fine powder. After the components have been ground they are pressed into a pellet and subjected to hot isostatic pressing. Hot isostatic pressing utilizes an inert gas, primarily argon, in a sealed oven. This ...
Ceramic forming techniques include throwing, slipcasting, tape casting, freeze-casting, injection molding, dry pressing, isostatic pressing, hot isostatic pressing (HIP), 3D printing and others. Methods for forming ceramic powders into complex shapes are desirable in many areas of technology.
The expanded graphite can be used to make graphite foil or used directly as a "hot top" compound to insulate molten metal in a ladle or red-hot steel ingots and decrease heat loss, or as firestops fitted around a fire door or in sheet metal collars surrounding plastic pipe (during a fire, the graphite expands and chars to resist fire ...
The ion-conductive β-alumina plays a key part in the battery cells performance, requiring development of optimal microstructure and purity to ensure beneficial electrical and mechanical properties. Current high-end manufacturing methods for producing the β-alumina electrolytes includes: isostatic pressing and electrophoretic deposition (EDP).
Hot pressing is a high-pressure, low-strain-rate powder metallurgy process for forming of a powder or powder compact at a temperature high enough to induce sintering and creep processes. [1] This is achieved by the simultaneous application of heat and pressure. Hot pressing is mainly used to fabricate hard and brittle materials.
Isostatic presses can be either high speed, high output type of automatic presses for such parts as ceramic insulators for spark plugs or sand blast nozzles, or slower operating "wet bag" presses that are much more manual in operation but suitable particularly for large machinable blanks or blanks that will be cut or otherwise formed in ...