Free-electron lasers have been developed for use in X-ray diffraction and crystallography. [27] These are the brightest X-ray sources currently available; with the X-rays coming in femtosecond bursts. The intensity of the source is such that atomic resolution diffraction patterns can be resolved for crystals otherwise too small for collection.
X-ray reflectivity is an analytical technique for determining thickness, roughness, and density of single layer and multilayer thin films. Wide-angle X-ray scattering (WAXS), a technique concentrating on scattering angles 2θ larger than 5°. Spectrum of various inelastic scattering processes that can be probed with inelastic X-ray scattering ...
The use of computational methods for the powder X-ray diffraction data analysis is now generalized. It typically compares the experimental data to the simulated diffractogram of a model structure, taking into account the instrumental parameters, and refines the structural or microstructural parameters of the model using least squares based ...
D positions are calculated using Bragg’s law but because clay mineral analysis is one dimensional, l can substitute n, making the equation l λ = 2d sin Θ. When measuring the x-ray diffraction of clays, d is constant and λ is the known wavelength from the x-ray source, so the distance from one 00l peak to another is equal. [3]
It is an X-ray-diffraction [2] method and commonly used to determine a range of information about crystalline materials. The term WAXS is commonly used in polymer sciences to differentiate it from SAXS but many scientists doing "WAXS" would describe the measurements as Bragg/X-ray/powder diffraction or crystallography.
The Scherrer equation, in X-ray diffraction and crystallography, is a formula that relates the size of sub-micrometre crystallites in a solid to the broadening of a peak in a diffraction pattern. It is often referred to, incorrectly, as a formula for particle size measurement or analysis. It is named after Paul Scherrer.
Compared with destructive techniques, e.g. three-dimensional electron backscatter diffraction (3D EBSD), [5] with which the sample is serially sectioned and imaged, 3DXRD and similar X-ray nondestructive techniques have the following advantages: They require less sample preparation, thus limiting the introduction of new structures in the sample.