Ferritic stainless steels [2] [3] are a family of stainless steels [4] with a body-centered cubic (BCC) crystal structure and composed primarily of iron and chromium. They are characterized by being magnetic, non-hardenable by heat treating, and having excellent resistance to stress-corrosion cracking (SCC).
The average carbon footprint of stainless steel (all grades, all countries) is estimated to be 2.90 kg of CO 2 per kg of stainless steel produced, [88] of which 1.92 kg are emissions from raw materials (Cr, Ni, Mo); 0.54 kg from electricity and steam, and 0.44 kg are direct emissions (i.e., by the stainless steel plant). Note that stainless ...
304 stainless steel is also used in the architectural field for exterior accents such as water and fire features. It is also a common coil material for vaporizers. Early SpaceX Starships used SAE 301 stainless steel in their construction, [8] before moving over to SAE 304L for the SN7 test tank [broken anchor] [9] and Starship SN8 in 2020. [10]
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.
X46Cr13 is the European Norm name for a common martensitic stainless steel with the numeric name 1.4034. It is equivalent to American Iron and Steel Institute standard 420C. It has the highest carbon content of the SAE 420 series. [1] [2] [3]
Pitting resistance equivalent number (PREN) is a predictive measurement of a stainless steel's resistance to localized pitting corrosion based on its chemical composition. In general: the higher PREN-value, the more resistant is the stainless steel to localized pitting corrosion by chloride.
300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless steel is Type 304, also known as 18/8 or A2. Type 304 is extensively used in such items as cookware, cutlery, and kitchen equipment. Type 316, also known as A4, is the next most common austenitic stainless steel.