Spring steel is a name given to a wide range of steels [1] used in the manufacture of different products, including swords, saw blades, springs and many more. These steels are generally low-alloy manganese , medium-carbon steel or high-carbon steel with a very high yield strength .
Mangalloy, also called manganese steel or Hadfield steel, is an alloy steel containing an average of around 13% manganese. Mangalloy is known for its high impact strength and resistance to abrasion once in its work-hardened state.
Spiegeleisen (manganese, carbon, silicon) Staballoy (stainless steel) (manganese, chromium, carbon) - see also Uranium below; Steel (Category:Steels) Bulat steel; Chromoly (chromium, molybdenum) Crucible steel; Damascus steel; Ducol; Hadfield steel; High-speed steel. Mushet steel; HSLA steel; Maraging steel; Reynolds 531; Silicon steel ; Spring ...
80CrV2 is commonly known as Swedish Saw Steel. It is a manganese-vanadium steel with 0.8% carbon content, making it a true high-carbon steel; and as such is easily hardened able, and with very good edge retention. It has an excellent reputation for toughness and shock resistance, comparable to S7 steel.
Hadfield steel, named after Robert Hadfield, or manganese steel, contains 12–14% manganese which, when abraded, strain-hardens to form a very hard skin which resists wearing. Uses of this particular alloy include tank tracks , bulldozer blade edges, and cutting blades on the jaws of life .
Manganese mostly dissolves in ferrite forming MnS, MnO•SiO 2, but also carbides: (Fe,Mn) 3 C. Chromium forms partitions between the ferrite and carbide phases in steel, forming (Fe,Cr 3)C, Cr 7 C 3, and Cr 23 C 6. The type of c#arbide that chromium forms depends on the amount of carbon and other alloying elements present.
Phosphate conversion coating is a chemical treatment applied to steel parts that creates a thin adhering layer of iron, zinc, or manganese phosphates to improve corrosion resistance or lubrication or as a foundation for subsequent coatings or painting. [1] [2] [3] It is one of the most common types of conversion coating.
The embrittlement decreases at higher manganese concentrations and reaches an acceptable level at 8%. Steel containing 8 to 15% of manganese has a high tensile strength of up to 863 MPa. [77] [78] Steel with 12% manganese was discovered in 1882 by Robert Hadfield and is still known as Hadfield steel (mangalloy).