In US use, the grade designation is equal to the minimum yield strength of the bar in ksi (1000 psi); for example, grade 60 rebar has a minimum yield strength of 60 ksi. Rebar is most commonly manufactured in grades 40, 60, and 75 with higher strength readily available in grades 80, 100, 120 and 150. Grade 60 (420 MPa) is the most widely used ...
For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi).
304 stainless steel cannot be heat treated—instead it can be strengthened by cold working. It is weakest in the annealed condition, and is strongest in the full-hard condition. The tensile yield strength ranges from 210 to 1,050 MPa (30,000 to 153,000 psi).
EN 10027-1 steel grade designation system. ... So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i ...
The SAE steel grades system is a standard alloy numbering system (SAE J1086 – Numbering Metals and Alloys) for steel grades maintained by SAE International.. In the 1930s and 1940s, the American Iron and Steel Institute (AISI) and SAE were both involved in efforts to standardize such a numbering system for steels.
A572 Steel Material Properties, Per ASTM Standards [2]; A572 Grade Yield Point (KSI) [MPa] Tensile Strength (KSI) [MPa] Min. 8” Elongation % Grade 42
ASTM A992 is currently the most available steel type for structural wide-flange beams. The industry's technical institute describes the standard thus: "ASTM A992 (Fy = 50 ksi, Fu = 65 ksi) is the preferred material specification for wide-flange shapes, having replaced ASTM A36 and A572 grade 50. There are a couple of noteworthy enhancements ...
It has a yield strength up to 80,000 psi (550 MPa) but costs only 24% more than A36 steel (36,000 psi (250 MPa)). One of the disadvantages of this steel is that it is 30 to 40% less ductile . In the U.S., these steels are dictated by the ASTM standards A1008/A1008M and A1011/A1011M for sheet metal and A656/A656M for plates.