HY-80 is a high-tensile, high yield strength, low alloy steel. It was developed for use in naval applications, specifically the development of pressure hulls for the US nuclear submarine program and is still currently used in many naval applications. It is valued for its strength to weight ratio. [citation needed]
The yield strength or yield stress is a material property and is the stress corresponding to the yield point at which the ... Steel, high strength alloy ASTM A514: 690:
A514 is a particular type of high strength steel, which is quenched and tempered alloy steel, with a yield strength of 100,000 psi (100 ksi or approximately 700 MPa). The ArcelorMittal trademarked name is T-1. [1] A514 is primarily used as a structural steel for building construction.
The next set of 3 digits gives the steel's minimum yield strength. So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered by the relevant standard – i.e. EN10025. [2] Below is a table indicating the most common application codes.
Low-rate yield strength is 216,000 psi (1,489 MPa), and low-rate ultimate strength is 270,200 psi (1,863 MPa). By comparison, ordinary structural steel has a yield strength of 36,000 psi, 4150 "ordnance" steel (used in high-quality military gun barrels) has a yield strength of 75,000 psi.
Spring steel is a name given to a wide range of steels [1] used in the manufacture of different products, including swords, saw blades, springs and many more. These steels are generally low-alloy manganese , medium-carbon steel or high-carbon steel with a very high yield strength .
The 32 grades have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). The 36 grades have yield strength of 51,000 psi (355 MPa), and ultimate tensile strength of 71,000 - 90,000 psi (490-620 MPa). Per Steel Vessel Rules Part 2 Chapter 1 Section 3 Table 2 (pg 36).
440C (UNS designation S44004) is a martensitic 400 series stainless steel, [1] and has the highest carbon content of the 400 stainless steel series. It can be heat treated to reach hardness of 58 to 60 HRC.