Hardening is a metallurgical metalworking process used to increase the hardness of a metal. The hardness of a metal is directly proportional to the uniaxial yield stress at the location of the imposed strain. A harder metal will have a higher resistance to plastic deformation than a less hard metal.
Induction heating is a non contact heating process which uses the principle of electromagnetic induction to produce heat inside the surface layer of a work-piece. By placing a conductive material into a strong alternating magnetic field, electric current can be made to flow in the material thereby creating heat due to the I 2 R losses in the material.
Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel.
At 0-D there is precipitate and solid solution strengthening with particulates strengthening structure, at 1-D there is work/forest hardening with line dislocations as the hardening mechanism, and at 2-D there is grain boundary strengthening with surface energy of granular interfaces providing strength improvement.
A forming limit diagram, also known as a forming limit curve, is used in sheet metal forming for predicting forming behavior of sheet metal. [1] [2] The diagram attempts to provide a graphical description of material failure tests, such as a punched dome test. In order to determine whether a given region has failed, a mechanical test is performed.
Schematic cutaway view of a diffusion hardened metal gear. Diffusion hardening is a process used in manufacturing that increases the hardness of steels.In diffusion hardening, diffusion occurs between a steel with a low carbon content and a carbon-rich environment to increase the carbon content of the steel and ultimately harden the workpiece.
To examine a piece of steel, obtain a hand file and file an edge of the selected metal. If the piece of steel has not undergone the hardening process, the metal file should easily 'bite' into the sample. If the metal has been hardened, the file fails to cut into the sample and glances off with little visible effect.
The finish on a Glock pistol is the third and final hardening process. It is 0.05 mm (0.0020 in) thick and produces a 64 Rockwell C hardness rating via a 500 °C (932 °F) nitride bath. [ 33 ] The final matte, non-glare finish meets or exceeds stainless steel specifications, is 85% more corrosion resistant than a hard chrome finish, and is 99.9 ...