HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
The high molecular weight makes it a very tough material, but results in less efficient packing of the chains into the crystal structure as evidenced by densities of less than high-density polyethylene (for example, 0.930–0.935 g/cm 3). UHMWPE can be made through any catalyst technology, although Ziegler catalysts are most common.
High-density polyethylene (HDPE) has a very low degree of branching, is relatively stiff, and is used in applications such as bullet-proof vests. Low-density polyethylene (LDPE), on the other hand, has significant numbers of both long and short branches, is relatively flexible, and is used in applications such as plastic films. Dendrimer and ...
These molecules are several orders of magnitude longer than those of familiar high-density polyethylene (HDPE) due to a synthesis process based on metallocene catalysts, resulting in UHMWPE molecules typically having 100,000 to 250,000 monomer units per molecule each compared to HDPE's 700 to 1,800 monomers.
Resin code for polyethylene terephthalate Polypropylene lid of a Tic Tac box, with a living hinge and the resin identification code, 5, under its flap. The Resin Identification Code (RIC) is a technical standard with a set of symbols appearing on plastic products that identify the plastic resin out of which the product is made. [1]
[17] Piping systems for the conveyance of water, chemicals or gases are commonly produced in Polypropylene, and to a much greater extent Polyethylene. Piping systems in high-density Polyethylene (HDPE, PE100, PE80) are fast becoming the most commonly used drinking water, waste water and natural gas distribution piping systems in the world.
Polyethylene (polyethene, polythene, PE) is a family of similar materials categorized according to their density and molecular structure. It is also known as poly and is obtained by the addition polymerisation of ethylene. It may be of low density or high density depending upon the process used in its manufacturing.
The degradation of polyethylene occurs by random scission—a random breakage of the bonds that hold the atoms of the polymer together. When heated above 450 °C, polyethylene degrades to form a mixture of hydrocarbons. In the case of chain-end scission, monomers are released and this process is referred to as unzipping or depolymerization ...