Broadly, modern glass container factories are three-part operations: the "batch house", the "hot end", and the "cold end". The batch house handles the raw materials; the hot end handles the manufacture proper—the forehearth, forming machines, and annealing ovens; and the cold end handles the product-inspection and packaging equipment.
The key advantage of this technique as compared to the float glass process is that the pristine surfaces are not touched by molten tin. The technique is used for the production of very thin flat panel display glass by the companies Asahi Glass Co. , Corning , Nippon Electric Glass , [ 1 ] Samsung Corning Precision Materials , and various other ...
Machine drawn cylinder sheet was the first mechanical method for "drawing" window glass. Cylinders of glass 40 feet (12 m) high are drawn vertically from a circular tank. The glass is then annealed and cut into 7 to 10 foot (2 to 3 m) cylinders. These are cut lengthways, reheated, and flattened. This process was invented in the US in 1903.
The Fourcault process is a method of manufacturing plate glass. First developed in Belgium by Émile Fourcault [ fr ] (1862–1919) during the early 1900s, the process was used globally. Fourcault is an example of a "vertical draw" process, in that the glass is drawn against gravity in an upward direction. [ 1 ]
Main page; Contents; Current events; Random article; About Wikipedia; Contact us
Cutter removing ends of cylinder and slicing the tube lengthwise Sliced tube of glass is flattened in an oven. Cylinder blown sheet is a type of hand-blown window glass. It is created with a similar process to broad sheet, but with the use of larger cylinders. In this manufacturing process glass is blown into a cylindrical shape by a glass blower.
By Leah Douglas and Julie Steenhuysen (Reuters) -California's public health department reported a possible case of bird flu in a child with mild respiratory symptoms on Tuesday, but said there was ...
Float glass is a sheet of glass made by floating molten glass on a bed of molten metal of a low melting point, typically tin, [1] although lead was used for the process in the past. [2] This method gives the sheet uniform thickness and a very flat surface. [ 3 ]